THYOSIL E1589


Selfcrosslinking acrylic emulsion自交联丙烯酸乳液
Description描述

THYOSIL E1589 is an acrylic emulsionpolymer designed for aqueous high gloss enamels with excellent appearance andoutstanding resistance.
是一款水性丙烯酸乳液聚合物,为外层高光耐侯性能所设计

Characteristics 特点
·        The excellent selfcrosslinking technology provides good hardness, high gloss and durability
·        优异的自交联技术 提供来了高硬度,高光,耐候性能。
·        The low solvent required toformulate offers improved performance, appearance and resistance properties.
·        低溶剂配方提供了优异的性能,外观,以及各种耐性。

Advantages优势
ü      Excellent alkyd adhesion, wet and dry 优异的粘合性,干湿性
ü      Excellent block resistance and durability 优异的防结皮性和持久性
ü      High gloss 高光
ü      Very good resistance to household chemicals.好的耐各种家用化学品腐蚀性能
ü      Low coalescent  and co-solvent demand 仅需少量的成膜助剂和助溶剂。

Typical properties典型值
These properties are typical, do notconstitute specifications

Appearance外观

Milky white liquid奶白色液体

Solids % 固含量

45

pH

8.5

Viscosity a 25oC (cP) 粘度

500

MFFT (oC) 成膜温度

24






Starting Formulations基础配方


1)    High gloss varnish 高光漆

It
RAW MATERIAL原料
FORMULA %
1

THYOSILE1589
90,00
2

THYON PW7 聚乙烯蜡乳液
0,50
3

BYK-346流平剂
0,10
4

BUTIL CELLOSOLVE丁基纤维素
2,00
5

WATER
5,50
6

NX / 795成膜助剂(酯醇)
1,00
7

IPEL BP20杀菌剂
0,15
8

IPEL FBP2100防霉剂
0,25
9

TAFIGEL PUR80聚氨酯流平剂
0,30
10

BYK-024 消泡剂
0,20

TOTAL
100,00


1 & 2:Diransa, 3 & 10: Byk Additives, 6: Perstop, 7 & 8: Itibanyl Productos Especiales <st1:country-region w:st="on">S.A., 9: Münzing Chemie GMBH


Typical properties: 典型值

Test测试
Results

Solid Content           固含量

40%

Viscosity Ford Cup N°4 at 25°C粘度

70 sec

pH

8.5






Application应用

·        A smooth surface is obtained by sanding the woodwith #150-320 grit sandpaper. # 150- 320砂纸把木头的表面打磨光滑
·        A first layer of primer is required. 按需要先上底漆
·        After drying the first coating, sand the surfacewith #320 grit sandpaper. 油完第一层后,等到它变干。然后使用# 320砂纸打磨
·        Allow the layer to dry 2 hours before re-coating.
·        预涂的底漆干后2小时后再上面漆
·        When the previous coat has dried, recoat withanother layer.
·        当先前的涂层干后再上另层。
·        A minimum of two coats is suggested; allow thecoating to dry 24 hours before use. It is recommended to wait 7 days beforeperforming the quality tests.
·        建议至少涂2遍,在使用之前需干燥24小时以上。建议7天后测试性能品质。

Test测试

Result结果

Dry Time 干燥时间

3 hours   小时 (25°C and 50%  Relative humidity)
25°C 50%的相对湿度

Water Spot  水滴

Good

Resistance 耐性(抗性)

Very Good非常好 (Chemicals household家用化学品)

Gloss ( Glossmeter)亮度

20° 84            60° 84            85° 96

Blocking Resistance抗结皮

Excellent 优异       (dry 24 hours24小时)

Adhesion  Ericksen附着力

Excellent 优异       (7 days before)7天后

Levelling 流平性

Very Good 非常好 (dry 24 hours)24小时

Sand between layers沙层之间

Very Good 非常好(dry 24 hours, #320 grindsandpaper)
24小时后,用320号砂纸打磨

Recoat 重涂

Excellent优异       (Old alkyd varnish旧的醇酸漆)

















2)     Satin varnish缎漆(哑光)
It
RAWMATERIAL
FORMULA%配比
1

THYOSIL E1589
88,00
2

THYON PW7 聚乙烯蜡分散液
0,50
3

BYK-346流平剂
0,10
4

AGUA
6,90
5

BUTIL CELLOSOLVE丁基纤维素
2,00
6

NX / 795成膜助剂(酯醇)
1,00
7

IPEL BP20 杀菌剂
0,15
8

IPEL FBP2100防霉剂
0,25
9

TAFIGEL PUR80聚氨酯流平剂
0,30
10

BYK-024 消泡剂
0,20
11

SYLOID 244气相微粉硅胶
0,60

TOTAL
100,00























1 & 2:Diransa, 3 & 10: Byk Additives, 6: Perstop, 7 & 8: Itibanyl ProductosEspeciales <st1:country-region w:st="on">S.A.,9:  Münzing Chemie GMBH, 11: Greace.

Application 应用

·        A smooth surface is obtained by sanding the woodwith #150-320 grit sandpaper. # 150- 320砂纸把木头的表面打磨光滑
·        A first layer of primer is required. 按需要先上底漆
·        After drying the first coating, sand the surfacewith #320 grit sandpaper.油完第一层后,等到它变干。然后使用# 320砂纸打磨
·        Allow the layer to dry 2 hours before re-coating.
·        预涂的底漆干后2小时后再上面漆
·        When the previous coat has dried, recoat withanother layer.
·        A minimum of two coats is suggested; allow thecoating to dry 24 hours before use. It is recommended to wait 7 days beforeperforming the quality tests.
·        建议至少涂2遍,在使用之前需干燥24小时以上。建议7天后测试性能品质。


Typical properties典型值

Test测试
Result

Solid Content           固含量

40%

Viscosity Ford Cup N°4 at 25°C      粘度 福特4号杯

70 sec

pH

8.5






Test

Result

Dry Time干燥时间

3 hours          (25°C and 50%  Relative humidity)
3小时 25°C 50%的相对湿度

Water Spot 水滴

Good

Resistance耐性(抗性)

VeryGood 非常好(Chemicals household    家用化学品)

Gloss ( Glossmeter)亮度

20°24            60° 57            85° 85

Blocking Resistance抗结皮

Excellent优异       (dry 24 hours24小时)

Adhesion Ericksen附着力

Excellent优异       (7 days before)7天后

Levelling流平性

Very Good非常好(dry 24 hours24小时)

Sand between layers沙层之间

Very Good 非常好(dry 24 hours, #320 grind sandpaper) 24小时 #320号砂纸

Recoat重涂

Excellent优异(Old alkyd varnish旧的醇酸漆)



Formulation tips配方提示

» Low coalescent demand 需要少许成膜助剂
THYOSIL E1589 has low coalescing solvents demand over other acrylicpolymers.
The selection of an optimum coalescing system depends on the required drying rate,temperature and relative humidity. It is suggested8% to 10% of coalescing agents based on solids for proper film formation. Itmay be used lower levels depending on the porosity of the substrate, ambienthumidity and other solvents used in the formulation.      Reducing the amount of coalescent allows faster drying but anexcessive reduction may result in poorer film formation and consequently theloss of mechanical strength, lack of brightness, etc.It is recommended to allowformulations to equilibrate for at least 8 hours, to obtain representativeresults in the tests performed.
E1589 需要少许成膜溶剂,根据所需要的干燥速度,温度和湿度,选择最佳的配比。通常推荐使用 8%10%的成膜助剂(与配方中E1589的固含量相比),也可以低于或高于此水平,取决于基材的具体特性,环境湿度以及其它配方中的溶剂含量等条件。减少成膜助剂的使用干燥速度会快,但若添加太少会影响成膜性,同时还会减少防污性能和减少机械强度,缺少亮度。配成后要8小时后测试结果没有变化。

» Rheology Modifiers流变改性剂
Suitable polyurethane thickeners are recommended. Keepin mind that the efficiency of urethane associative thickeners depends on thecoalescing solvents chosen.  Differentrheological modifiers should be tested to achieve a good balance of performanceand application properties of the dried film.
我们推荐使用聚亚氨酯增稠剂,记住聚氨酯缔合增稠剂的效果取决于成膜助剂的选择。不同的流变改性剂会影响性能和成膜的特性

» Defoamers消泡剂
Check thoroughly different commercial defoamers.Fisheye defects or loss in transparency and gloss can occur if an excess doseis chosen.
消泡剂的使用要根据不同情况提前测试,添加过量会导致鱼眼的产生或膜的透明度

» Wetting agents润湿剂
Flow and levelling properties are improved by using wettingagents.     使用润湿剂可以改善流平性
These additives must be adjusted carefully as microfoam generally causes defects. Moreover THYOSIL E1589 has an excellent wetting force and generally it does not require support wetting additives.
添加润湿剂需要非常谨慎不然会产生微泡影响品质。THYOSIL E1589本身具有很好的润湿能力通常不需要添加润湿剂。

» Surface modifiers表面改性剂
Appropriate anticratering additivesmay be added.  Resistance to scratch canbe improved.
可以适当的添加抗缩孔添加剂可以提高抗划伤性能

» Biocides 杀菌剂
THYOSIL E1589 is protectedagainst bacteria and fungi attack by using 0.15% of IPEL BP20*. It is suggested to use IPEL FBP2100* at 0.25% forprotection against fungi and algae film (*Itibanyl Productos Especiales <st1:country-region w:st="on">S.A.).
为防止细菌和真菌的滋生可以添加 0.15% IPEL BP20* 。为防止真菌和藻类可以添加 0.25% IPEL FBP2100*

Safe handling and storage Information

Beforeusing this product, read the Material Safety Data Sheet